Cores Cores Amorphous Nanocrystalline Cores

Product numerus

Core magnitudine

Si magnitudo

ferrum crucis

sectionem

medium iter longum

pondus

nominis inductionem

OD x ID x HT

OD

ID

HT

AFe

lFe*

mFe

10 kHz

100 kHz

mmxmmxmm

mm

mm

mm

cm2

cm

g

μH

HTC-15*10*6

15 x 10 x6

18.0

8.4

9.3

0.12

3.9

3.4

32

7.3

LTC-15*10*6

15 x 10 x6

18.0

8.4

9.3

0.12

3.9

3.4

11.7

6.5

HTC-25*20*10

25 x 20 x 10

27.7

18.1

12.8

0.2

7.1

10

28.4

7.3

HTC-25*15*10

25 x 15 x 10

28.1

13.2

12.3

0.4

6.28

18

70

16

HTC-25*16*10

25 x 16 x 10

27.6

13.8

12.6

0.36

6.4

17

65.5

15.5

LTC-25*16*10

25 x 16 x 10

27.6

13.8

12.6

0.36

6.4

17

17

11.5

HTC-30*20*10

30 x 20 x 10

33.1

17.7

13.3

0.4

7.9

23

59.3

14

LTC-30*20*10

30 x 20 x 10

33.1

17.7

13.3

0.4

7.9

23

15.5

11.1

HTC-30*20*15

30 x 20 x15

33.6

17.8

17.8

0.57

7.9

33

88

20

HTC-40*32*15

40 x 32 x 15

44.9

28.6

18.8

0.46

11.3

38

47.2

11.1

LTC-40*32*15

40 x 32 x 15

44.9

28.6

18.8

0.46

11.3

38

13

8.4

HTC-40*25*15

40 x 25 x 15

43.9

21.5

18.7

0.86

10.2

64

101

23.1

HTC-40*32*15

45 x 30 x 15

48.5

26.7

17.8

0,86

11.8

74

87.5

20.3

LTC-40*32*15

45 x 30 x 15

48.5

26.7

17.8

0,86

11.8

74

24.3

15.9

HTC-50*40*20

50 x 40 x 20

53.6

37.1

23.1

0.76

14.1

79

70

15

HTC-59*40*20

59 x 40 x 20

63.7

36.8

24.4

1.52

15.5

165

80

20

HTC-65*50*25

65 x 50 x 25

68.2

46.5

28.5

1.5

18.0

190

58.6

18.1

HTC-80*50*20

80 x 50 x 20

83.9

46.8

24.7

2.28

20.4

342

94

28

HTC-90*60*20

90 x 60 x 20

93.5

55.1

24.5

2.28

23.6

395

81

25.1

HTC-102*76*25

102 x 76 x 25

107.3

59.6

30.4

2.47

28

508

68.8

21.6

Bs（T）

1.2

Hc A/m）

<2

Tc（℃）

570

Tx（℃）

500

opus temperatus℃

-55～130

Damnum P（20kHz，0.5T），（W/kg）

<20